High temperature ceramic paste
ANTI-SEIZE COMPOSITE COMPOUND WITH HIGH SOLID LUBRICANTS CONTENT
Technical ceramic technology (Si3N4)
Boron nitride nanopowder (Hex.BN)
Tungsten disulphide (WS2)
White lubricant compound for dynamic lubrication at high temperature
High temperature assembly ans disassembly paste, metal free, no electrolytical coupling effect
without metal loading
DESCRIPTION
Facilitates the assembly and disassembly of components and assemblies subject to high temperatures or aggressive environments. Effective for use in thin layers.
Excellent dynamic film strength.
Enables life-long static surface treatment.
Guarantee to contain no metal salts, metalloids, or nitrites.
High-temperature, anti-corrosion lubricant.
Efficient in static applications and when subject to vibratory phenomena.
Not for use on slow-moving bearings or rollers without regular top-up of lubricant.
APPLICATIONS
Plastic moulding, injection, composite forming.
Screwed assemblies, even with destruction of thread.
Steam connections. Cable glands. Mechanical bushes.
Impregnation of sealing braids. O-ring seals.
Smooth bearings on hot bending machines. Superheating valves.
Turbines. Combustion engines. Compressors. Gas generators. Foundry ejectors. Aluminium extrusion (start prior to die coating) Zamak de-moulding.
Vulcanised mould closures. Oven door hinges.
INSTRUCTIONS FOR USE
Apply in thin layers on clean surfaces. De-grease beforehand and if necessary components to treat, with Neutralène® V200 in aerosol form. Spray from 15 to 25 cm depending on the component dimensions.
TYPICAL PHYSICAL-CHEMICAL PROPERTIES
|
PHYSICAL PROPERTIES OF GREASE |
|||
|
PROPERTY |
STANDARD or METHOD |
VALUE |
UNITS |
|
Appearance |
Visual |
Paste |
- |
|
Colour |
Visual |
White |
- |
|
Apparent density at 25°C (Pycnometer) |
NF T 30,020 |
1260 |
kg/m³ |
|
NLGI category |
NLGI National Lubricating Grease Institute |
2 |
Category according to penetration |
|
Soap/Gelling agent |
- |
Inorganic |
- |
|
Nature of solid lubricants |
- |
Si3N4 - NB - WS2 |
12% |
|
Penetration at 25°C Not worked Worked, 60 strokes Worked, 1000 strokes Worked, 10,000 strokes Worked, 100,000 strokes |
NF ISO 2137 / ASTM 2176
|
265-295 265-295 265-295 275-305 275-305 |
1/10° mm 1/10° mm 1/10° mm 1/10° mm 1/10° mm |
|
Drop point Drop point if higher than 360°C |
NF ISO 2176 / ASTM D 566 ASTM D 2265 |
>250 - |
°C
|
|
Impurities > 25µ > 75µ > 125µ |
FMTS 791 3005 |
0 0 0 |
number/ml number/ml number/ml |
|
PHYSICAL-CHEMICAL PROPERTIES OF BASE OIL |
|||
|
PROPERTY |
STANDARD or METHOD |
VALUE |
UNITS |
|
Nature of base oil |
- |
Polymer |
- |
|
Kinematic viscosity at 40°C Kinematic viscosity at 100°C |
NF EN ISO 3104 |
140 100 |
mm/s־¹ mm/s־¹ |
|
Acid index Ia |
NF ISO 6618 |
0.36 |
mg KOH/l |
|
PERFORMANCE CHARACTERISTICS |
|||
|
CHARACTERISTIC |
STANDARD or METHOD |
VALUE |
UNITS |
|
Oil separation 7 days at 40°C (bleeding) |
NF T 60,191 |
1 |
% mass |
|
Oil separation 24h at 41kPa (bleeding under pressure) |
ASTM D 1742 |
<2 |
% mass |
|
Sulphated ash |
NF T 60,144 |
0 |
% mass |
|
Copper blade corrosion |
ASTM D 4048 |
1a |
Measured value |
|
Hoffman oxidation |
ASTM D 942 |
<10 |
psi |
|
Loss by evaporation 22h at 121°C |
ASTM D 972 |
0 |
% mass |
|
Loss by Noack evaporation |
NF T 60 101 CEC L-40 A-93 ASTM D5800 |
<0.5 |
% mass |
|
Elastomer swelling 70 h at 100 °C |
ASTM D 4289.83 |
<0.8 |
% dimensional change |
|
Static temperature ranges In neutral atmospheres In oxidizing atmospheres |
- - |
-25 +1200 -25 +900 |
°C °C |
|
Rotation factor |
n.dm |
80.000 |
mm.min-1 |
|
4 balls test Impression diameter Weld load index |
ASTM D 2266 / ISO 20 623 |
0.55 5500 |
mm daN |
|
TIMKEN test |
ASTM D 2509 |
40 |
Ibs |
|
EMCOR anti-rust test Dynamic Static |
NF T 60 135 ISO DP 6294/ ASTM D 1743 |
0 2 |
Measured value Measured value |
|
Water wash-off resistance at 80°C |
ASTM 1264 |
<1 |
% mass |
|
ADDITIONAL CHARACTERISTICS |
|||
|
PROPERTY |
STANDARD or METHOD |
VALUE |
UNITS |
|
Tightening torque at 20°C |
MIL A 907 E 80 |
80 |
Newton metre |
|
Release torque at 450°C |
MIL A 907 E 80 |
80 |
Newton metre |
|
Release torque at 750°C |
MIL A 907 E 80 |
90/95 |
Newton metre |
* not measured or not measurable
PRESENTATION
|
|
Aérosol 650 ml
|
Looking for another product?
|
Discover our entire range by clicking on the photo |
.jpg)
Manufacturing, lubrification, cleansing, protection,
IBiotec® Tec Industries® Service
offers a wide range of products reserved for industrial area
If you wish for :
a free sample
a technical advice
a product data sheet
a safety data sheet
IBiotec® Tec Industries®Service
manufacturer of technical chemical products.
Welcome to our website.
IBiotec® Tec Industries®Service is on : 